The steel used in sword production is known as tamahagane (玉鋼:たまはがね), or "jewel steel" (tama – ball or jewel, hagane – steel). Tamahagane is produced from iron sand, a source of iron ore, and mainly used to make samurai swords, such as the katana, and some tools. Diagram of a tatara and bellows
Tamahagane (玉鋼) is a general term for steel, not used prior to the Meiji Era, literally meaning "precious steel". Steel is smelted at Shimane facility for Japanese swords (nihontō (日本刀), commonly known as katana (刀)) by contemporary Japanese forge masters like Kihara Akira and Gassan Sadatoshi is still smelted in a tatara.
The word tama means 'precious', and the word hagane means 'steel'. [1] Tamahagane is used to make Japanese swords, daggers, knives, and other kinds of tools. The carbon content of the majority of analyzed Japanese swords historically lies between a mass of 0.5–0.7%; however, the range extends up to 1.5%. [2] [3]
5160, a spring steel. Popular steel for forging swords and large knives, with high toughness and good wear resistance. [citation needed] Popular sword manufacturers that use 5160 spring steel include Hanwei and Generation 2. [citation needed] 5160 spring steel is mainly used on Medieval type swords. [citation needed] 4140 [definition needed]
The peak of Toledo steel production was seen in the 15th and 16th centuries, and by the end of the Reconquista, Toledo was considered to be the greatest sword-making centre in the world. [ 3 ] [ 5 ] And while Toledo steel set the standard for excellence of European weapons, there were also very few locales that surpassed Toledo in terms of ...
A diagram of a katana and koshirae with components identified. Fuchi (縁): The fuchi is a hilt collar between the tsuka and the tsuba.; Habaki (鎺): The habaki is a wedge-shaped metal collar used to keep the sword from falling out of the saya and to support the fittings below; fitted at the ha-machi and mune-machi which precede the nakago.
This allows the sword to have the strength and the ability to hold a sharp edge, as well as to cause the sword to tend to bend rather than flex under stress. The process starts in the combining of the iron and carbon, by heating iron sand to 1200-1500 degrees Celsius in a traditional furnace, or tatara , for 72 hours.