The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [8] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.
Annealed 6061 (6061-O temper) has maximum ultimate tensile strength no more than 150 MPa (22 ksi), [7] [8] and maximum yield strength no more than 83 MPa (12 ksi) [7] or 110 MPa (16 ksi). [8] The material has elongation (stretch before ultimate failure) of 10–18%.
5154 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. 5154 aluminium is commonly used in welded structures such as pressure vessels and ships.
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
The search engine that helps you find exactly what you're looking for. Find the most relevant information, video, images, and answers from all across the Web.
The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting. It is commonly heat treated to produce tempers with a higher strength at the expense of ductility. [1] Alternate names and designations include AlSiMg and A96005.