In the paint and coating industries, paint adhesion testing is often used to determine if the paint or coating will adhere properly to the substrates to which they are applied. Several tests measure the resistance of paints and coatings from substrates: cross-cut test, scrape adhesion, pull-off test , and others.
Bresle patch injected with 15ml water as in ISO 8502-6 Annex A. The ISO 8502-6 standard prescribes in annex A that certified patches shall be used. This annex describes a stress test to ensure patch adhesion and wash ability. Not being supplied with a certificate that the patches pass this test will render the results obtained by these patches ...
Dye penetrant inspection (DP), also called liquid penetrate inspection (LPI) or penetrant testing (PT), is a widely applied and low-cost inspection method used to check surface-breaking defects in all non-porous materials (metals, plastics, or ceramics).
A pull-off test, also called stud pull test, is a type of test in which an adhesive connection is made between a stud and a carrier (or object to be tested) by using a glue, possibly an epoxy or polyester resin, that is stronger than the bond that needs to be tested.
The salt spray test (or salt fog test) is a standardized and popular corrosion test method, used to check corrosion resistance of materials and surface coatings.Usually, the materials to be tested are metallic (although stone, ceramics, and polymers may also be tested) and finished with a surface coating which is intended to provide a degree of corrosion protection to the underlying metal.
Hydrostatic testing is the most common method employed for testing pipes and pressure vessels. Using this test helps maintain safety standards and durability of a vessel over time. Newly manufactured pieces are initially qualified using the hydrostatic test. They are then revalidated at regular intervals according to the relevant standard.
Depending on the FBE coating system, full cure can be achieved in less than one minute to few minutes in case of long cure FBE's, which are used for internal pipe coating applications. Rebars are coated in a similar manner as coating application, on the exterior of pipes. For FBE coating application on the interior of pipe surface, a lance is used.
In adhesion tests per ASTM D4541, in which an aluminum stud is bonded to the test surface and the stud is pulled in the direction normal to the surface, both surfaces of the failure interface were analyzed by X-ray photoelectron spectroscopy (XPS). F/C ratio was used as an indicator of the failure mode: F/C of zero corresponds to failure in the ...