Making a saline water solution by dissolving table salt in water.The salt is the solute and the water the solvent. In chemistry, a solution is defined by IUPAC as "A liquid or solid phase containing more than one substance, when for convenience one (or more) substance, which is called the solvent, is treated differently from the other substances, which are called solutes.
The IUPAC definition of a solid solution is a "solid in which components are compatible and form a unique phase". [3]The definition "crystal containing a second constituent which fits into and is distributed in the lattice of the host crystal" given in refs., [4] [5] is not general and, thus, is not recommended.
Solute atoms should have a smaller radius than 59% of the radius of solvent atoms. [5] [6] The solute and solvent should have similar electronegativity. [7] Valency factor: two elements should have the same valence. The greater the difference in valence between solute and solvent atoms, the lower the solubility.
The solubility of a specific solute in a specific solvent is generally expressed as the concentration of a saturated solution of the two. [1] Any of the several ways of expressing concentration of solutions can be used, such as the mass, volume, or amount in moles of the solute for a specific mass, volume, or mole amount of the solvent or of the solution.
Also acid ionization constant or acidity constant. A quantitative measure of the strength of an acid in solution expressed as an equilibrium constant for a chemical dissociation reaction in the context of acid-base reactions. It is often given as its base-10 cologarithm, p K a. acid–base extraction A chemical reaction in which chemical species are separated from other acids and bases. acid ...
Most of the solute does not dissociate in a weak electrolyte, whereas in a strong electrolyte a higher ratio of solute dissociates to form free ions. A weak electrolyte is a substance whose solute exists in solution mostly in the form of molecules (which are said to be "undissociated"), with only a small fraction in the form of ions.
In materials science, segregation is the enrichment of atoms, ions, or molecules at a microscopic region in a materials system. While the terms segregation and adsorption are essentially synonymous, in practice, segregation is often used to describe the partitioning of molecular constituents to defects from solid solutions, [1] whereas adsorption is generally used to describe such partitioning ...
Some alloying elements are only soluble in small amounts, whereas some solvent and solute pairs form a solution over the whole range of binary compositions. Generally, higher solubility is seen when solvent and solute atoms are similar in atomic size (15% according to the Hume-Rothery rules) and adopt the same crystal structure in