If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect. Case hardened steel-Vickers hardness test. Case hardened articles starting as low carbon steel (0.5 - 1.5% carbon content) can also be labeled hardened steel.
Hardened AW-6060 Aluminium: 75 HB Mild steel: 120 HB 18–8 (304) stainless steel annealed: 200 HB [3] Quenched and tempered steel wear plate: 400-700 HB Hardened tool steel: 600–900 HB (HBW 10/3000) Glass: 1550 HB Rhenium diboride: 4600 HB Note: Standard test conditions unless otherwise stated
Steel, stainless steels, hard cast irons, pearlitic malleable iron, titanium, titanium alloys, deep case-hardened steel, other materials harder than 100 HRB: 100: 500 D: HRD: 100: spheroconical diamond † Thin steel and medium case-hardened steel and pearlitic malleable iron: 100: 500 E: HRE: 100: 1 ⁄ 8 in (3.18 mm) ball
MIL-DTL-46100E specifies a steel of identical hardness. [3] MIL-DTL-32332 specifies ultra-hard steel, with Brinell hardness in excess of 570. [3] A Chinese publication lists 30MnCrNiMo "685" steel as the material used in Chinese rolled armor plates, with a Brinell Hardness of HBW 444-514 (thin) / 429-495 (thick).
Colt Peacemaker, showing discoloration from case-hardening. Case-hardening or carburization is the process of introducing carbon to the surface of a low-carbon iron, or more commonly a low-carbon steel object, in order to harden the surface. Iron which has a carbon content greater than ~0.02% is known as steel.
Hardening is a metallurgical metalworking process used to increase the hardness of a metal. The hardness of a metal is directly proportional to the uniaxial yield stress at the location of the imposed strain. A harder metal will have a higher resistance to plastic deformation than a less hard metal.
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
Type 440—a higher grade of cutlery steel, with more carbon, allowing for much better edge retention when properly heat-treated. It can be hardened to approximately Rockwell 58 hardness, making it one of the hardest stainless steels. Due to its toughness and relatively low cost, most display-only and replica swords or knives are made of 440 ...