Colloidal silica gel with light opalescence. Silica gel is an amorphous and porous form of silicon dioxide (silica), consisting of an irregular tridimensional framework of alternating silicon and oxygen atoms with nanometer-scale voids and pores. The voids may contain water or some other liquids, or may be filled by gas or vacuum.
Schuetze reagent, also written as Schütze reagent, is made up of iodine pentoxide (I 2 O 5) and sulfuric acid on granular silica gel.It is used to convert carbon monoxide (CO) into carbon dioxide (CO 2) at room temperature. [1]
Sodium Metasilicate reacts with acids to produce silica gel. [6] Cements and Binders - dehydrated sodium metasilicate forms cement or binding agent. Pulp and Par - sizing agent and buffer/stabilizing agent when mixed with hydrogen peroxide. Soaps and Detergents - as an emulsifying and suspension agent.
In M-SG an alkali metal is absorbed into silica gel at elevated temperatures. The resulting black powder material is an effective reducing agent and safe to handle as opposed to the pure metal. The material can also be used as a desiccant and as a hydrogen source. [1] The metal is either sodium or a sodium - potassium alloy (Na 2 K).
In acidic solutions, the silicate ions react with hydrogen ions to form silicic acids, which tend to decompose into hydrated silicon dioxide gel. [citation needed] Heated to drive off the water, the result is a hard translucent substance called silica gel, widely used as a desiccant. It can withstand temperatures up to 1100 °C. [citation needed]
Colloidal silicas are most often prepared in a multi-step process where an alkali-silicate solution is partially neutralized, leading to the formation of silica nuclei. The subunits of colloidal silica particles are typically in the range of 1 to 5 nm. Whether or not these subunits are joined depends on the conditions of polymerization.
In contrast, silica gel can be regenerated by heating it in a regular oven to 120 °C (250 °F) for two hours. However, some types of silica gel will "pop" when exposed to enough water. However, some types of silica gel will "pop" when exposed to enough water.
Precipitated silica is an amorphous form of silica (silicon dioxide, SiO 2); it is a white, powdery material. Precipitated silica is produced by precipitation from a solution containing silicate salts. The three main classes of amorphous silica are pyrogenic silica, precipitated silica and silica gel.