Ceramic forming techniques are ways of forming ceramics, which are used to make everything from tableware such as teapots to engineering ceramics such as computer parts. Pottery techniques include the potter's wheel , slip casting and many others.
These forming techniques are well known for providing tools and other components with dimensional stability, surface quality, high (near theoretical) density and microstructural uniformity. The increasing use and diversity of specialty forms of ceramics adds to the diversity of process technologies to be used. [11]
Ceramic material is an inorganic, metallic oxide, nitride, or carbide material. Some elements, such as carbon or silicon, may be considered ceramics. Ceramic materials are brittle, hard, strong in compression, and weak in shearing and tension. They withstand the chemical erosion that occurs in other materials subjected to acidic or caustic ...
Slip casting, or slipcasting, is a ceramic forming technique, and is widely used in industry and by craft potters to make ceramic forms. This technique is typically used to form complicated shapes like figurative ceramics that would be difficult to be reproduced by hand or other forming techniques. [1]
Ceramic molding is a versatile and precise manufacturing process that transforms clay or porcelain into intricate shapes. Employing techniques like slip casting or press molding, artisans create precise replicas of original models. After molding, the ceramics are fired at high temperatures, ensuring durability and aesthetic appeal.
Compaction of ceramic powders is a forming technique for ceramics in which granular ceramic materials are made cohesive through mechanical densification, either by hot or cold pressing. The resulting green part must later be sintered in a kiln. The compaction process permits an efficient production of parts to close tolerances with low drying ...
Chemical vapour infiltration (CVI) is a ceramic engineering process whereby matrix material is infiltrated into fibrous preforms by the use of reactive gases at elevated temperature to form fiber-reinforced composites. [1] The earliest use of CVI was the infiltration of fibrous alumina with chromium carbide. [2]
Ceramic mold casting, also known ambiguously as ceramic molding, [1] is a group of metal casting processes that use ceramics as the mold material. It is a combination of plaster mold casting and investment casting. [2] [3] There are two types of ceramic mold casting: the Shaw process and the Unicast process. [4]