A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
A Rockwell hardness tester. The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
Newmark's Influence Chart is an illustration used to determine the vertical pressure at any point below a uniformly loaded flexible area of soil of any shape. This method, like others, was derived by integration of Boussinesq's equation for a point load.
The principle behind the test is that the mean pressure required to test the material is the measurement of the hardness of the material. Units of megapascals (MPa) are frequently used for reporting Meyer hardness, but any unit of pressure can be used.
Indentation hardness tests compose the majority of processes used to determine material hardness, and can be divided into three classes: macro, micro and nanoindentation tests. [2] [3] Microindentation tests typically have forces less than 2 N (0.45 lb f). Hardness, however, cannot be considered to be a fundamental material property.
Soil particle density is typically 2.60 to 2.75 grams per cm 3 and is usually unchanging for a given soil. [44] Soil particle density is lower for soils with high organic matter content, [45] and is higher for soils with high iron-oxides content. [46]
Meyer's law is an empirical relation between the size of a hardness test indentation and the load required to leave the indentation. [1] The formula was devised by Eugene Meyer of the Materials Testing Laboratory at the Imperial School of Technology, Charlottenburg, Germany, circa 1908.
The unit of hardness given by the test is known as the Vickers Pyramid Number (HV) or Diamond Pyramid Hardness (DPH). The hardness number can be converted into units of pascals, but should not be confused with pressure, which uses the same units. The hardness number is determined by the load over the surface area of the indentation and not the ...