For many alloys, including carbon steel, the crystal grain size and phase composition, which ultimately determine the material properties, are dependent on the heating rate and cooling rate. Hot working or cold working after the annealing process alters the metal structure, so further heat treatments may
This produces steel that is much stronger than full-annealed steel, and much tougher than tempered quenched steel. However, added toughness is sometimes needed at a reduction in strength. Tempering provides a way to carefully decrease the hardness of the steel, thereby increasing the toughness to a more desirable point.
However, quenching certain steel too fast can result in cracking, which is why high-tensile steels such as AISI 4140 should be quenched in oil, tool steels such as ISO 1.2767 or H13 hot work tool steel should be quenched in forced air, and low alloy or medium-tensile steels such as XK1320 or AISI 1040 should be quenched in brine.
Martensitic stainless alloys are hardenable by heat treatment, specifically by quenching and stress relieving, or by quenching and tempering (referred to as QT). [9] [10] The alloy composition, and the high cooling rate of quenching enable the formation of martensite. Untempered martensite is low in toughness and therefore brittle.Tempered ...
Only steel that is high in carbon can be hardened and tempered. If a metal does not contain the necessary quantity of carbon, then its crystalline structure cannot be broken, and therefore the physical makeup of the steel cannot be altered. Frequently, the term "hardening" is associated with tempered steel. Both processes are used hand in hand ...
Mild steel: 120 HB 18–8 (304) stainless steel annealed: 200 HB [3] Quenched and tempered steel wear plate: 400-700 HB Hardened tool steel: 600–900 HB (HBW 10/3000) Glass: 1550 HB Rhenium diboride: 4600 HB Note: Standard test conditions unless otherwise stated
Steel which has a carbon content greater than ~0.25% can be direct-hardened by heating to around 600°C, and then quickly cooling, often by immersing in water or oil, known as quenching. Hardening is desirable for metal components because it gives increased strength and wear resistance, the tradeoff being that hardened steel is generally more ...
If a disordered state is not in thermodynamic equilibrium, one speaks of quenched disorder. For instance, a glass is obtained by quenching (supercooling) a liquid. By extension, other quenched states are called spin glass, orientational glass. In some contexts, the opposite of quenched disorder is annealed disorder.