Results from the WOW.Com Content Network
A higher ratio gives a too fluid concrete mix resulting in a too porous hardened concrete of poor quality. Often, the concept also refers to the ratio of water to cementitious materials, w/cm. Cementitious materials include cement and supplementary cementitious materials such as ground granulated blast-furnace slag (GGBFS), fly ash (FA), silica ...
Abrams' law (also called Abrams' water-cement ratio law) [1] is a concept in civil engineering. The law states the strength of a concrete mix is inversely related to the mass ratio of water to cement. [1] [2] As the water content increases, the strength of concrete decreases. Abrams’ law is a special case of a general rule formulated ...
Design-mix concrete can have very broad specifications that cannot be met with more basic nominal mixes, but the involvement of the engineer often increases the cost of the concrete mix. Concrete mixes are primarily divided into nominal mix, standard mix and design mix. Nominal mix ratios are given in volume of . Nominal mixes are a simple ...
The flow table test or slump-flow test is a method to determine consistency of fresh concrete. Flow table test is also used to identify transportable moisture limit of solid bulk cargoes. [ 1 ] It is used primarily for assessing concrete that is too fluid (workable) to be measured using the slump test , because the concrete will not retain its ...
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
Speed in the construction practices followed in ready mix concrete plant is followed continuously by having mechanized operations. The output obtained from a site mix concrete plant using a 8/12 mixer is 4 to 5 metric cubes per hour which is 30-60 metric cubes per hour in a ready mix concrete plant.
Abrams investigated the influence of the composition of concrete mixes on the strength of the end product. Some of the results of his research were: the definition of the concept of fineness modulus; the definition of the water–cement ratio; a test method for the workability of a concrete mix by using what the Abrams cone.
The test is carried out using a metal mould in the shape of a conical frustum known as a slump cone or Abrams cone, that is open at both ends and has attached handles.The tool typically has an internal diameter of 100 millimetres (3.9 in) at the top and of 200 millimetres (7.9 in) at the bottom with a height of 305 millimetres (12.0 in).The cone is placed on a hard non-absorbent surface.