6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Print/export Download as PDF; Printable version; In other projects Wikidata item; ... Tensile strength (annealed) 179 MPa Yield strength (annealed) ...
It has high toughness, high strength. It has high stress corrosion cracking resistance. [1] It has electric conductivity of value having 40 percent of copper. [2] 7050 aluminium is known as a commercial aerospace alloy. [3]
The alloy 3004 is commonly used in the making of beverage cans. It was developed to satisfy the need for thinner gauges in can-stock, and thereby to some extent replaced its predecessor 3003 alloy in the making of beverage cans. Can-stock can be made thinner due to the addition of 1% magnesium, which contributes in solid solution strengthening.
Download as PDF; Printable version; ... Aluminum: 97.3 ... Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa Yield strength 170 MPa ...
7068 alloy is a 7000 series aluminium-zinc alloy registered with the US Aluminium Association and produced to AMS 4331 (chemical composition and mechanical properties) and AMS 2772 (heat treatment). 7068 alloy ‘A’ and ‘B’ tensile data and fatigue properties have been ratified for inclusion in MIL Handbook 5 / MMPDS.
The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting. It is commonly heat treated to produce tempers with a higher strength at the expense of ductility. [1] Alternate names and designations include AlSiMg and A96005.