In this case, sacrificial anodes work as part of a galvanic couple, promoting corrosion of the anode, while protecting the cathode metal. In other cases, such as mixed metals in piping (for example, copper, cast iron and other cast metals), galvanic corrosion will contribute to accelerated corrosion of parts of the system.
The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the difference in ...
Galvanic corrosion is the electrochemical erosion of metals. Corrosion occurs when two dissimilar metals are in contact with each other in the presence of an electrolyte , such as salt water. This forms a galvanic cell, with hydrogen gas forming on the more noble (less active) metal.
The less noble metal is removed from the alloy by a microscopic-scale galvanic corrosion mechanism. The most susceptible alloys are the ones containing metals with high distance between each other in the galvanic series, e.g. copper and zinc in brass.
In the early 20th century, galvanized piping swiftly took the place of previously used cast iron and lead in cold-water plumbing. Practically, galvanized piping rusts from the inside out, building up layers of plaque on the inside of the piping, causing both water pressure problems and eventual pipe failure.
A galvanic anode, or sacrificial anode, is the main component of a galvanic cathodic protection system used to protect buried or submerged metal structures from corrosion. They are made from a metal alloy with a more "active" voltage (more negative reduction potential / more positive oxidation potential ) than the metal of the structure.
Sacrificial anodes made from iron attached to the copper sheath of the hull below the waterline dramatically reduced the corrosion rate of the copper. However, a side effect of cathodic protection was the increase in marine growth. Usually, copper when corroding releases copper ions which have an anti-fouling effect.
Galvanic corrosion of an aluminium plate occurred when the plate was connected to a mild steel structural support.. Galvanic corrosion occurs when two different metals have physical or electrical contact with each other and are immersed in a common electrolyte, or when the same metal is exposed to electrolyte with different concentrations.