Spontaneous glass breakage is a phenomenon by which tempered glass may spontaneously break without any apparent reason. The most common causes are: [13] [14] Internal defects within the glass such as nickel sulfide inclusions. Nickel sulfide defects can cause spontaneous breakage of tempered glass years after its manufacturing. [15]
Annealing is a process of slowly cooling hot glass objects after they have been formed, to relieve residual internal stresses introduced during manufacture. Especially for smaller, simpler objects, annealing may be incidental to the process of manufacture, but in larger or more complex products it commonly demands a special process of annealing in a temperature-controlled kiln known as a lehr. [1]
Magma rich in silica and poor in dissolved water is most easily cooled rapidly enough to form volcanic glass. As a result, rhyolite magmas, which are high in silica, can produce tephra composed entirely of volcanic glass and may also form glassy lava flows. [2] Ash-flow tuffs typically consist of countless microscopic shards of volcanic glass. [3]
Vitrification (from Latin vitrum 'glass', via French vitrifier) is the full or partial transformation of a substance into a glass, [1] that is to say, a non-crystalline or amorphous solid. Glasses differ from liquids structurally and glasses possess a higher degree of connectivity with the same Hausdorff dimensionality of bonds as crystals: dim ...
The glass–liquid transition, or glass transition, is the gradual and reversible transition in amorphous materials (or in amorphous regions within semicrystalline materials) from a hard and relatively brittle "glassy" state into a viscous or rubbery state as the temperature is increased. [2] An amorphous solid that exhibits a glass transition ...
Ninja rocks take advantage of the physical properties of tempered glass, disrupting surface compressive stress and causing the glass to shatter. Tempered glass, which is used for the side windows of most vehicles, is manufactured with an extremely high surface compressive stress and high internal tensile stress. This gives it strength and ...
Chicken wings have three parts, the drumette, the flat or wing, and the tip. Chicken wings can be cooked in a variety of ways and are often fried or deep fried. Food explorers looking for ...
Prince Rupert's drops have remained a scientific curiosity for nearly 400 years due to two unusual mechanical properties: [4] when the tail is snipped, the drop disintegrates explosively into powder, whereas the bulbous head can withstand compressive forces of up to 664,300 newtons (67,740 kg f).