Chemical coloring of metals is the process of changing the color of metal surfaces with different chemical solutions. The chemical coloring of metals can be split into three types: electroplating – coating the metal surface with another metal using electrolysis. patination – chemically reacting the metal surface to form a colored oxide or ...
Electroplating, also known as electrochemical deposition or electrodeposition, is a process for producing a metal coating on a solid substrate through the reduction of cations of that metal by means of a direct electric current.
In some cases, it is desirable to co-deposit two or more metals resulting in an electroplated alloy deposit. Depending on the alloy system, an electroplated alloy may be solid solution strengthened or precipitation hardened by heat treatment to improve the plating's physical and chemical properties. Nickel-Cobalt is a common electroplated alloy.
100 ml of distilled water cathode made of platinum or stainless steel (needle), anode nickel-plated or gold-plated copper or brass or polished steel, duration 10 s, distance between cathode and anode 3 mm . [20] An electrolyte of 100 g of litharge dissolved in 0.5 l of water can also be used in which 100 g of NaOH is dissolved.
In some fuel cells, a solid electrolyte or proton conductor connects the plates electrically while keeping the hydrogen and oxygen fuel gases separated. [28] In electroplating tanks, the electrolyte simultaneously deposits metal onto the object to be plated, and electrically connects that object in the circuit.
Copper electroplating takes place in an electrolytic cell using electrolysis. As with all plating processes, the part to be plated must be cleaned before depositing metal to remove soils, grease, oxides, and defects. [4] [5] After precleaning, the part is immersed in the cell's aqueous electrolyte solution and functions as the cathode.
Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used. [1]
The metal is deposited on the cathode. In a practical sense, this idealized process is complicated by some or all of the following considerations: the metal content is low (a few percent is typical), other metals deposit competitively with the desired one, the ore is not easily or efficiently dissolved.