6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Due to its high strength and fatigue resistance, 2024 is widely used in aircraft, especially wing and fuselage structures under tension. [6] [7] Additionally, since the material is susceptible to thermal shock, 2024 is used in qualification of liquid penetrant tests outside of normal temperature ranges.
7068 alloy is a 7000 series aluminium-zinc alloy registered with the US Aluminium Association and produced to AMS 4331 (chemical composition and mechanical properties) and AMS 2772 (heat treatment). 7068 alloy ‘A’ and ‘B’ tensile data and fatigue properties have been ratified for inclusion in MIL Handbook 5 / MMPDS.
Aluminum: 97.3 Silicon: 1 Magnesium: 0.80 Manganese: 0.5 Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa Yield strength ...
For deep draw and complex shapes, and for the avoidance of spring-back, an aluminium hot stamping process (Hot Form Quench) can be used, which forms a blank at a elevated temperature (~ 550 C) in a cooled die, leaving a part in W-temper condition before artificial aging to the T6 full strength state.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
Print/export Download as PDF; Printable version; In other projects Wikidata item; ... Tensile strength (annealed) 179 MPa Yield strength (annealed) ...