The rotary kiln was invented in 1873 by Frederick Ransome. [1] He filed several patents in 1885-1887, but his experiments with the idea were not a commercial success. Nevertheless, his designs provided the basis for successful kilns in the US from 1891, subsequently emulated worldwide.
The Waelz process is a method of recovering zinc and other relatively low boiling point metals from metallurgical waste (typically electric arc furnace flue dust) and other recycled materials using a rotary kiln (waelz kiln). The zinc enriched product is referred to as waelz oxide, and the reduced zinc by product as waelz slag.
Lightweight expanded clay aggregate (LECA) or expanded clay (exclay) is a lightweight aggregate made by heating clay to around 1,200 °C (2,190 °F) in a rotary kiln. The heating process causes gases trapped in the clay to expand, forming thousands of small bubbles and giving the material a porous structure.
Rotary kilns run 24 hours a day, and are typically stopped only for a few days once or twice a year for essential maintenance. One of the main maintenance works on rotary kilns is tyre and roller surface machining and grinding works which can be done while the kiln works in full operation at speeds up to 3.5 rpm.
The multiple hearth furnaces consist of several circular hearths or kilns superimposed on each other. Material is fed from the top and is moved by the action of rotating "rabble arms", and the revolving mechanical rabbles attached to the arms move over the surface of each hearth to continuously shift the ore.
View of the six rotary furnaces at the Essen–Borbeck direct reduction plant, c. 1964. The Krupp–Renn process was a direct reduction steelmaking process used from the 1930s to the 1970s. It used a rotary furnace and was one of the few technically and commercially successful direct reduction processes in the world, acting as an alternative to ...
Calcination is thermal treatment of a solid chemical compound (e.g. mixed carbonate ores) whereby the compound is raised to high temperature without melting under restricted supply of ambient oxygen (i.e. gaseous O 2 fraction of air), generally for the purpose of removing impurities or volatile substances and/or to incur thermal decomposition.
Four Seger cones after use. Pyrometric cones are pyrometric devices that are used to gauge heatwork during the firing of ceramic materials in a kiln. The cones, often used in sets of three, are positioned in a kiln with the wares to be fired and, because the individual cones in a set soften and fall over at different temperatures, they provide a visual indication of when the wares have reached ...