Stainless steel is a steel, and as such its melting point is near that of ordinary steel, and much higher than the melting points of aluminium or copper. As with most alloys, the melting point of stainless steel is expressed in the form of a range of temperatures, and not a single temperature. [9]
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Martensitic stainless steels can be high- or low-carbon steels built around the composition of iron, 12% up to 17% chromium, carbon from 0.10% (Type 410) up to 1.2% (Type 440C): [ 9] Up to about 0.4%C they are used mostly for their mechanical properties in applications such as pumps, valves, and shafts.
Ferritic stainless steel[ 2][ 3] forms one of the five stainless steel families, the other four being austenitic, martensitic, duplex stainless steels, and precipitation hardened. [ 4] For example, many of AISI 400-series of stainless steels are ferritic steels. By comparison with austenitic types, these are less hardenable by cold working ...
Superalloy. A superalloy, or high-performance alloy, is an alloy with the ability to operate at a high fraction of its melting point. [ 1] Key characteristics of a superalloy include mechanical strength, thermal creep deformation resistance, surface stability, and corrosion and oxidation resistance. The crystal structure is typically face ...
As more steel is produced than is scrapped, the amount of recycled raw materials is about 40% of the total of steel produced - in 2016, 1,628,000,000 tonnes (1.602 × 10 9 long tons; 1.795 × 10 9 short tons) of crude steel was produced globally, with 630,000,000 tonnes (620,000,000 long tons; 690,000,000 short tons) recycled.
Argon oxygen decarburization. Argonoxygen decarburization ( AOD) is a process primarily used in stainless steel making and other high grade alloys with oxidizable elements such as chromium and aluminium. After initial melting the metal is then transferred to an AOD vessel where it will be subjected to three steps of refining; decarburization ...
Over 80% of the world's ferrochrome is utilised in the production of stainless steel. In 2006, 28,000,000 tons of stainless steel were produced. [3] [4] Stainless steel depends on chromium for its appearance and resistance to corrosion. Average chrome content in stainless steel is approx. 18%. It is also used to add chromium to carbon steel ...