Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used. [1]
Before plating, the surface of the material must be thoroughly cleaned. Unwanted solids left on the surface cause poor plating. Cleaning is usually achieved by a series of chemical baths, including non-polar solvents to remove oils and greases, as well as acids and alkalis to remove oxides, insoluble organics, and other surface contaminants.
Electroless nickel-boron plating developed as a variant of the similar nickel-phosphorus process, discovered accidentally by Charles Adolphe Wurtz in 1844. [2]In 1969, Harold Edward Bellis from DuPont filed a patent for a general class of electroless plating processes using sodium borohydride, dimethylamine borane, or sodium hypophosphite, in the presence of thallium salts, thus producing a ...
Electroless nickel plating uses nickel salts as the metal cation source and either hypophosphite (H 2 PO 2-) (or a borohydride-like compound) as a reducer. [5] A side reaction forms elemental phosphorus (or boron) which is incorporated in the coating. The classical deposition methods follows the following steps:
Electroless nickel immersion gold (ENIG or ENi/IAu), also known as immersion gold (Au), chemical Ni/Au or soft gold, is a metal plating process used in the manufacture of printed circuit boards (PCBs), to avoid oxidation and improve the solderability of copper contacts and plated through-holes.
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
It can be used on copper and its alloys, silver, nickel, iron, gold. The color depends on the duration of immersion, the sequence of colors on brass: Golden yellow-copper-purple-dark, blue-light, blue-chrome-nickel-red-grey, blue, and gray-black to iron or carbon steel. [32]
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...