In materials science, a thermosetting polymer, often called a thermoset, is a polymer that is obtained by irreversibly hardening ("curing") a soft solid or viscous liquid prepolymer . [1] Curing is induced by heat or suitable radiation and may be promoted by high pressure or mixing with a catalyst .
Thermosetting plastics are polymer materials which are liquid or malleable at low temperatures, but which change irreversibly to become hard at high temperatures. Subcategories This category has only the following subcategory.
Condensites are similar thermoset materials having much the same properties, characteristics, and uses. [77] Crystalate is an early plastic. [78] Faturan is a phenolic resin, also similar to Bakelite, that turns red over time, regardless of its original color. [79] Galalith is an early plastic derived from milk products. [80]
A thermoset polymer matrix is a synthetic polymer reinforcement where polymers act as binder or matrix to secure in place incorporated particulates, fibres or other reinforcements. They were first developed for structural applications, [ 1 ] such as glass-reinforced plastic radar domes on aircraft and graphite - epoxy payload bay doors on the ...
Thermosets, or thermosetting polymers, can melt and take shape only once: after they have solidified, they stay solid and retain their shape permanently. [16] If reheated, thermosets decompose rather than melt. Examples of thermosets include epoxy resin, polyimide, and Bakelite. The vulcanization of rubber is an example of this process.
An acrylic resin is a thermoplastic or thermosetting plastic substance typically derived from acrylic acid, methacrylic acid and acrylate monomers such as butyl acrylate and methacrylate monomers such as methyl methacrylate. Thermoplastic acrylics designate a group of acrylic resins typically containing both a high molecular weight and a high ...
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
The polymer chains associate by intermolecular forces, which weaken rapidly with increased temperature, yielding a viscous liquid. In this state, thermoplastics may be reshaped, and are typically used to produce parts by various polymer processing techniques such as injection molding , compression molding , calendering , and extrusion .