Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel). [6] The Japanese equivalent grade of this material is SUS304.
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5]
In addition to the descriptive steel grade naming system indicated above, within EN 10027-2 is defined a system for creating unique steel grade numbers. While less descriptive and intuitive than the grand names they are easier to tabulate and use in data processing applications. The number is in the following format: x.yyzz(zz)
Carbon steels lack the chromium content of stainless steel, making them very susceptible to corrosion. [7] Carbon steels have less carbon than typical stainless steels, but it is the main alloy element. They are more homogeneous than stainless than other high alloy steels, having carbide only in very small inclusions in the iron.
UNS K11547 is T2 tool steel; UNS S17400 is ASTM grade 630, Cr-Ni 17-4PH precipitation hardened stainless steel; UNS S30400 is SAE 304, Cr/Ni 18/10, Euronorm 1.4301 stainless steel; UNS S31600 is SAE 316; UNS S31603 is 316L, a low carbon version of 316. The digits "03" were assigned since the maximum allowed carbon content is 0.03%; UNS C90300 ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), or rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5% or more chromium content, which forms a passive film that can protect the material ...
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...