In materials science, creep (sometimes called cold flow) is the tendency of a solid material to undergo slow deformation while subject to persistent mechanical stresses. It can occur as a result of long-term exposure to high levels of stress that are still below the yield strength of the material. Creep is more severe in materials that are ...
The basic design of a creep machine is the furnace, loading device and support structure. The main type of creep testing machine is a constant load creep testing machine. The constant load creep machine consists of a loading platform, foundation, fixture devices and furnace. The fixture devices are the grips and pull rods. [4]
Nabarro-Herring creep has a weak stress dependence. Coble creep, or grain-boundary diffusion, is the diffusion of vacancies occurs along grain-boundaries to elongate the grains along the stress axis. Coble creep has a stronger grain-size dependence than Nabarro–Herring creep, and occurs at lower temperatures while remaining temperature dependent.
L. M. Kachanov [5] and Y. N. Rabotnov [6] suggested the following evolution equations for the creep strain ε and a lumped damage state variable ω: ˙ = ˙ ˙ = ˙ where ˙ is the creep strain rate, ˙ is the creep-rate multiplier, is the applied stress, is the creep stress exponent of the material of interest, ˙ is the rate of damage accumulation, ˙ is the damage-rate multiplier, and is ...
Creep is the flow of material at high temperatures Fatigue is crack growth and propagation due to repeated loading Oxidation is a change in the chemical composition of the material due to environmental factors.
Creep and stress relaxation measures the elasticity, viscoelasticity and viscous behaviour of materials under a selected stress and temperature. Tensile geometry is the most common for creep measurements. A small force is initially imparted to keep the specimen aligned and straight.
For some materials, e.g. elastomers and polymers, subjected to large deformations, the engineering definition of strain is not applicable, e.g. typical engineering strains greater than 1%, [1] thus other more complex definitions of strain are required, such as stretch, logarithmic strain, Green strain, and Almansi strain.
Diffusion creep is caused by the migration of crystalline defects through the lattice of a crystal such that when a crystal is subjected to a greater degree of compression in one direction relative to another, defects migrate to the crystal faces along the direction of compression, causing a net mass transfer that shortens the crystal in the ...