Calcium silicate, also known as slag, is produced when molten iron is made from iron ore, silicon dioxide and calcium carbonate in a blast furnace. When this material is processed into a highly refined, re-purposed calcium silicate aggregate, it is used in the remediation of acid mine drainage (AMD) on active and passive mine sites. [13]
Calcium ions then react with the soluble sodium silicate gel to convert it into solid calcium silicate hydrates (C-S-H). The C-S-H forms a continuous poorly permeable coating at the external surface of the aggregate. The penetrated alkaline solution (NaOH / KOH) converts the remaining siliceous minerals into bulky soluble alkali silicate gel.
Only calcium silicates contribute to the strength. Tricalcium silicate is responsible for most of the early strength (first 7 days). [3] Dicalcium silicate, which reacts more slowly, only contributes to late strength. Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water.
Ground granulated blast furnace slag is a latent hydraulic binder forming calcium silicate hydrates (C-S-H) after contact with water. It is a strength-enhancing compound improving the durability of concrete. It is a component of metallurgic cement (CEM III in the European norm EN 197).
Alkali–silicate reaction, and; Alkali–carbonate reaction. The alkali–silica reaction is the most common form of alkali–aggregate reaction. Two other types are: the alkali–silicate reaction, in which layer silicate minerals (clay minerals), sometimes present as impurities, are attacked, and;
Cement hydration and strength development mainly depend on two silicate phases: tricalcium silicate (C 3 S) , and dicalcium silicate (C 2 S) . [1] Upon hydration, the main reaction products are calcium silicate hydrates (C-S-H) and calcium hydroxide Ca(OH) 2, written as CH in the cement chemist notation. C-S-H is the phase playing the role of ...
Actual formula Name or mineral phase CH: Ca(OH) 2 or CaO · H 2 O: Calcium hydroxide (portlandite) C-S-H: 0.6–2.0 CaO · SiO 2 · 0.9–2.5 H 2 O, with variable composition within this range, and often also incorporating partial substitution of Al for Si: Calcium silicate hydrate: C-A-H: Phase more complex than C-S-H: Calcium aluminate ...
The major raw material for the clinker-making is usually limestone mixed with a second material containing clay as a source of alumino-silicate. An impure limestone containing clay or silicon dioxide (SiO 2) can be used. The calcium carbonate (CaCO 3) content of these limestones can be as low as 80% by weight. During the calcination process ...