Ti-6Al-4V titanium alloy commonly exists in alpha, with hcp crystal structure, (SG : P63/mmc) and beta, with bcc crystal structure, (SG : Im-3m) phases. While mechanical properties are a function of the heat treatment condition of the alloy and can vary based upon properties, typical property ranges for well-processed Ti-6Al-4V are shown below.
Grade 37 contains 1.5% aluminium. Grade 38 contains 4% aluminium, 2.5% vanadium, and 1.5% iron. This grade was developed in the 1990s for use as an armor plating. The iron reduces the amount of Vanadium needed as a beta stabilizer. Its mechanical properties are very similar to Grade 5, but has good cold workability similar to grade 9. [35]
A titanium cylinder of quality "grade 2" Titanium is used in steel as an alloying element (ferro-titanium) to reduce grain size and as a deoxidizer, and in stainless steel to reduce carbon content. [11] Titanium is often alloyed with aluminium (to refine grain size), vanadium, copper (to harden), iron, manganese, molybdenum, and other metals. [96]
In the direct powder rolling (DPR) process BE powder is used to produce sheet and plate and composite multilayered sheet and plates. Sheets between 1.27 and 2.54 mm and 50 to 99+% dense of single layer CP titanium, Ti Grade 5, TiAl (Ti-48Al-2Cr-2Nb) and composite Ti/Grade 5/Ti and Grade 5/TiAl/Grade 5 have been produced by DPR and sintering.
Titanium aluminide (chemical formula TiAl), commonly gamma titanium, is an intermetallic chemical compound. It is lightweight and resistant to oxidation [1] and heat, but has low ductility. The density of γ-TiAl is about 4.0 g/cm 3. It finds use in several applications including aircraft, jet engines, sporting equipment and automobiles.
[7] As shown in the above table, alloying is one of the effective methods to improve the mechanical properties and since Niobium belongs to the same group of Vanadium in the periodic table it is of course acts as α –β stabilizing elements (similar to Ti-6Al-4V alloy), however the strength of Nb alloy is little less than that of Ti-6Al-4V .The main difference between Ti-6Al-4V and Ti-6Al ...
Titanium Beta C refers to Ti Beta-C, a trademark for an alloy of titanium originally filed by RTI International. [1] It is a metastable "beta alloy" which was originally developed in the 1960s; Ti-3Al-8V-6Cr-4Mo-4Zr, nominally 3% aluminum , 8% vanadium , 6% chromium , 4% molybdenum , 4% zirconium and balance (75%): titanium .
A UNS number only defines a specific chemical composition, it does not provided full material specification. Requirements such as material properties (yield strength, ultimate strength, hardness, etc.), heat treatment, form (rolled, cast, forged, flanges, tubes, bars, etc.), purpose (high temperature, boilers and pressure vessels, etc.) and testing methods are all specified in the material or ...