AlSi10Mg is a lightweight, high-strength aluminium alloy that is widely used in the aerospace, automotive, and medical industries. Its unique combination of aluminium , silicon , and magnesium makes it an ideal material for additive manufacturing processes, such as 3D printing .
In addition, there is the phase before the for the Aluminium-copper alloys are typical. Alloys with higher copper content (alloyings 6061, 6056, 6013) are mainly used in aviation. Iron occurs in all aluminium alloys as an impurity in quantities of 0.05-0.5%.
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.
1050 aluminium alloy; 1060 aluminium alloy; 1070 aluminium alloy; 1100 aluminium alloy; 1145 aluminium alloy; 1199 aluminium alloy; 1200 aluminium alloy; 1230 (VAD23) aluminium alloy; 1350 aluminium alloy; 1370 aluminium alloy; 2004 aluminium alloy; 2014 aluminium alloy; 2017 aluminium alloy; 2024 aluminium alloy; 2090 aluminium alloy; 2091 ...
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005 , 6061 , and 6063 ), although it is not strongly featured in ASTM (North American) standards.
Metal prices are the prices of metal as a commodity that are traded in bulk at a predefined purity or grade. Metal can be split into three major categories, precious metals, industrial metals and other metals. Precious metals and industrial metals are priced by trading of those metals on commodities exchanges. [1]
A billet is a length of metal that has a round or square cross-section, with an area less than 36 in 2 (230 cm 2). Billets are created directly via continuous casting or extrusion or indirectly via hot rolling an ingot or bloom. [1] [2] [4] Billets are further processed via profile rolling and drawing. Final products include bar stock and wire. [3]
Alusil as a hypereutectic aluminium-silicon alloy (EN AC-AlSi17Cu4Mg / EN AC-48100 or A390) contains approximately 78% aluminium and 17% silicon. [1] [2] This alloy was theoretically conceived in 1927 by Schweizer & Fehrenbach, [3] of Badener Metall-Waren-Fabrik, [4] but practically created only by Lancia [5] in the same year, for its car engines.