Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
Precipitation hardening (also called age hardening) is a process where a second phase that begins in solid solution with the matrix metal is precipitated out of solution with the metal as it is quenched, leaving particles of that phase distributed throughout to cause resistance to slip dislocations. This is achieved by first heating the metal ...
Heat treatment involves the use of heating or chilling, normally to extreme temperatures, to achieve the desired result such as hardening or softening of a material. Heat treatment techniques include annealing, case hardening, precipitation strengthening, tempering, carburizing, normalizing and quenching.
Subsequent aging (precipitation hardening) of the more common alloys for approximately 3 hours at a temperature of 480 to 500 °C (900 to 930 °F) produces a fine dispersion of Ni 3 (X,Y) intermetallic phases along dislocations left by martensitic transformation, where X and Y are solute elements added for such precipitation.
An example of the use of the nickel-based superalloys in the industrial field would be turbine blades. In practice, this alloy is known as MAR—M200 and is solid solution strengthened by chromium, tungsten and cobalt in the matrix and is also precipitation hardened by carbide and boride precipitates at the grain boundaries.
provides full-service NEPA 4. Qualifications and Experience Throughout the U.S., ERM support to private sector clients, federal agencies, and state
6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).