Understanding such properties is essential to making quality steel. At room temperature , the most stable form of pure iron is the body-centred cubic (BCC) structure called alpha iron or α-iron. It is a fairly soft metal that can dissolve only a small concentration of carbon, no more than 0.005% at 0 °C (32 °F) and 0.021 wt% at 723 °C ...
The properties of steel vary widely, depending on its alloying elements. The austenizing temperature, the temperature where a steel transforms to an austenite crystal structure, for steel starts at 900 °C (1,650 °F) for pure iron, then, as more carbon is added, the temperature falls to a minimum 724 °C (1,335 °F) for eutectic steel (steel ...
The properties of steel depend on its microstructure: the arrangement of different phases, some harder, some with greater ductility. At the atomic level, the four phases of auto steel include martensite (the hardest yet most brittle), bainite (less hard), ferrite (more ductile), and austenite (the most ductile). The phases are arranged by ...
European standard steel grade names fall into two categories: [1] Steel specified by purpose of use and mechanical properties. Steel specified by chemical composition. The inclusion of a letter 'G' before the code indicates the steel is specified in the form of a casting.
Carbon steel is heated to approximately 550 °C (1,000 °F) for 1 hour; this ensures the steel completely transforms to austenite. The steel is then air-cooled, which is a cooling rate of approximately 38 °C (100 °F) per minute. This results in a fine pearlitic structure, and a more-uniform structure.
A36 steel is a common structural steel alloy used in the United States. [1] The A36 (UNS K02600) standard was established by the ASTM International . The standard was published in 1960 and has been updated several times since. [ 2 ]
High-strength low-alloy steel (HSLA) is a type of alloy steel that provides better mechanical properties or greater resistance to corrosion than carbon steel.HSLA steels vary from other steels in that they are not made to meet a specific chemical composition but rather specific mechanical properties.
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...