A synthetic adsorbable suture material. Braided synthetic adsorbable multifilament made of polyglycolic acid and coated with N-laurin and L-lysine, which render the thread extremely smooth, soft and knot safe. A synthetic adsorbable suture material. Monofilament synthetic absorbable suture, prepared from the polyester, poly (p-dioxanone ...
Through many millennia, various suture materials were used or proposed. Needles were made of bone or metals such as silver, copper, and aluminium bronze wire. Sutures were made of plant materials (flax, hemp and cotton) or animal material (hair, tendons, arteries, muscle strips and nerves, silk, and catgut). [citation needed]
Materials in surgical sutures are textile based products. Suture material is frequently subdivided into absorbable thread and non-absorbable thread, and then into synthetic fibers and natural fibers. Whether a suture material is monofilament or polyfilament is an additional critical distinction. [55]
Prolene is a brand of synthetic polypropylene used in monofilament nonabsorbable sutures and meshes. The suture is indicated for skin closure and general soft tissue approximation and ligation. Its advantages include minimal tissue reactivity and durability.
Monocryl is a synthetic, absorbable suture manufactured in Cornelia, Georgia, USA, and trademarked by Ethicon. It is composed of poliglecaprone 25, which is a copolymer of glycolide and epsilon-caprolactone. [1] It comes both dyed (violet) and undyed (clear) and is an absorbable monofilament suture.
Ethilon is a synthetic nonabsorbable nylon suture manufactured by Ethicon in Cornelia, Georgia. Black in color, it is a monofilament suture that is used frequently for soft-tissue approximation and ligation. Even though it is nonabsorbable, the knot security decreases over time (in vivo) and should not be used where permanent retention is ...
For the production of sutures, polydioxanone is generally extruded into fibers, however care should be taken to process the polymer to the lowest possible temperature, in order to avoid its spontaneous depolymerization back to the monomer. The ether oxygen group in the backbone of the polymer chain is responsible for its flexibility.
Studies undergone using polyglycolide-made sutures have shown that the material loses half of its strength after two weeks and 100% after four weeks. The polymer is completely resorbed by the organism in a time frame of four to six months. [2] Degradation is faster in vivo than in vitro, this phenomenon thought to be due to cellular enzymatic ...