The corrosion of steel rebar is one of the main causes of premature failure of reinforced concrete structures worldwide, [4] mainly as a consequence of two degradation processes, carbonation and penetration of chlorides. [1] With regard to the corrosion degradation process, a simple and accredited model for the assessment of the service life is ...
Example of flat piece of concrete having dislodged with corroded rebar underneath, Welland River bridge across Queen Elizabeth Way in Niagara Falls, Ontario. The expansion of the corrosion products (iron oxides) of carbon steel reinforcement structures may induce internal mechanical stress (tensile stress) that cause the formation of cracks and disrupt the concrete structure.
Carbonatation induced rebar corrosion. Carbonatation is a slow process that occurs in concrete where lime (CaO, or Ca(OH) 2 ) in the cement reacts with carbon dioxide (CO 2) from the air and forms calcium carbonate. The water in the pores of Portland cement concrete is normally alkaline with a pH in the range of 12.5 to 13.5.
Rebar (short for reinforcement bar or reinforcing bar), known when massed as reinforcing steel or steel reinforcement, [1] is a tension device added to concrete to form reinforced concrete and reinforced masonry structures to strengthen and aid the concrete under tension.
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
In true corrosion fatigue, the fatigue-crack-growth rate is enhanced by corrosion; this effect is seen in all three regions of the fatigue-crack growth-rate diagram. The diagram on the left is a schematic of crack-growth rate under true corrosion fatigue; the curve shifts to a lower stress-intensity-factor range in the corrosive environment.
Corrosion loop(s) are systematized analysis "loops" used during Risk-based inspection analysis. Both terms “RBI Corrosion loops” or “RBI corrosion circuits” are generic terms used to indicate the systematization of piping systems into usable and understandable parts associated with corrosion.
In brief, corrosion is a chemical reaction occurring by an electrochemical mechanism (a redox reaction). [1] During corrosion of iron or steel there are two reactions, oxidation (equation 1), where electrons leave the metal (and the metal dissolves, i.e. actual loss of metal results) and reduction, where the electrons are used to convert oxygen and water to hydroxide ions (equation 2): [2]