6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. [ 2 ]
Aluminium–magnesium–silicon alloys (AlMgSi) are aluminium alloys—alloys that are mainly made of aluminium—that contain both magnesium and silicon as the most important alloying elements in terms of quantity. Both together account for less than 2 percent by mass.
6061 aluminum. Add languages. Add links. ... Upload file; Special pages; ... Get shortened URL; Download QR code; Print/export Download as PDF; Printable version ...
A UNS number only defines a specific chemical composition, it does not provided full material specification. Requirements such as material properties (yield strength, ultimate strength, hardness, etc.), heat treatment, form (rolled, cast, forged, flanges, tubes, bars, etc.), purpose (high temperature, boilers and pressure vessels, etc.) and testing methods are all specified in the material or ...
7068 alloy is a 7000 series aluminium-zinc alloy registered with the US Aluminium Association and produced to AMS 4331 (chemical composition and mechanical properties) and AMS 2772 (heat treatment). 7068 alloy ‘A’ and ‘B’ tensile data and fatigue properties have been ratified for inclusion in MIL Handbook 5 / MMPDS.
Aluminium is widely used in sheet metal form due to its flexibility, wide range of options, cost effectiveness, and other properties. [6] The four most common aluminium grades available as sheet metal are 1100-H14, 3003-H14, 5052-H32, and 6061-T6. [5] [7] Grade 1100-H14 is commercially pure aluminium, highly chemical and weather resistant.
Typical material properties for 6060 aluminum alloy include: [2] Density: 2.710 g/cm 3, or 169 lb/ft 3. Young's modulus: 70 GPa, or 10 Msi, or 303 EMEC; Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
Mn-free are very rare. Standard alloys are AlMg 3 Mn, AlMg 4.5 Mn 0.7, as well as for bodywork AlMg 4.5 Mn 0.4. Magnesium levels of up to 5% and manganese content up to 1% are used for wrought alloys. [8] [9] Mg contents up to 10% are also possible for cast alloys; however, contents of 7% and more are considered heavypourable. [10]