Strength allowables for this alloy are provided in Metallic Materials Properties Development and Standardization for design. [ 3 ] The main alloying elements are zinc (7.3 to 8.3%), magnesium (2.2 to 3.0%), copper (1.6 to 2.4%) and zirconium (0.05 to 0.15%), with traces of silicon, iron, manganese, chromium, and titanium.
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
It has high toughness, high strength. It has high stress corrosion cracking resistance. [1] It has electric conductivity of value having 40 percent of copper. [2] 7050 aluminium is known as a commercial aerospace alloy. [3]
The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting. It is commonly heat treated to produce tempers with a higher strength at the expense of ductility. [1] Alternate names and designations include AlSiMg and A96005.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Download as PDF; Printable version; ... Aluminum: 97.3 ... Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa Yield strength 170 MPa ...
Print/export Download as PDF; ... Aluminum: 91.5 - 95.5 Copper: 3.5 - 4.5 Iron: ... Tensile strength (annealed) 179 MPa Yield strength (annealed) ...
T651 temper 7075 has an ultimate tensile strength of 570 MPa (83,000 psi) and yield strength of 500 MPa (73,000 psi). It has a failure elongation of 3–9%. These properties can change depending on the form of material used. The thicker plates may exhibit lower strengths and elongation than the numbers listed above.