However, greater undercooling by rapid quenching results in formation of martensite or bainite instead of pearlite. This is possible provided the cooling rate is such that the cooling curve intersects the martensite start temperature or the bainite start curve before intersecting the P s curve. The martensite transformation being a ...
The specific cooling rate that is necessary to avoid the formation of pearlite is a product of the chemistry of the austenite phase and thus the alloy being processed. The actual cooling rate is a product of both the quench severity, which is influenced by quench media, agitation, load (quenchant ratio, etc.), and the thickness and geometry of ...
A cooling curve of naphthalene from liquid to solid. A cooling curve is a line graph that represents the change of phase of matter, typically from a gas to a solid or a liquid to a solid. The independent variable (X-axis) is time and the dependent variable (Y-axis) is temperature. [1] Below is an example of a cooling curve used in castings.
There are two types of continuous cooling diagrams drawn for practical purposes. Type 1: This is the plot beginning with the transformation start point, cooling with a specific transformation fraction and ending with a transformation finish temperature for all products against transformation time for each cooling curve.
English: The cooling curve and phase diagram of an alloy; in this case a copper/nickel alloy. Based on a diagram from Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4 .
Differential thermal analysis (DTA) is a thermoanalytic technique that is similar to differential scanning calorimetry.In DTA, the material under study and an inert reference are made to undergo identical thermal cycles, (i.e., same cooling or heating programme) while recording any temperature difference between sample and reference. [1]
English: Example of a cooling curve of a pure metal or eutectic alloy, with various aspects pointed out. Based on image from Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4.
The upper curve is the line of liquidus, and the lower curve is the line of solidus. In chemistry , materials science , and physics , the liquidus temperature specifies the temperature above which a material is completely liquid, [ 2 ] and the maximum temperature at which crystals can co-exist with the melt in thermodynamic equilibrium .