However, it is not beyond doubt that the passage describes deliberate quench-hardening, rather than simply cooling. [8] Likewise, there is a prospect that the Mahabharata refers to the oil-quenching of iron arrowheads, but the evidence is problematic. [9] Pliny the Elder addressed the topic of quenchants, distinguishing the water of different ...
The hardenability of a ferrous alloy is measured by a Jominy test: a round metal bar of standard size (indicated in the top image) is transformed to 100% austenite through heat treatment, and is then quenched on one end with room-temperature water. The cooling rate will be highest at the end being quenched, and will decrease as distance from ...
The quenching is required since the material otherwise would start the precipitation already during the slow cooling. This type of precipitation results in few large particles rather than the, generally desired, profusion of small precipitates. Precipitation hardening is one of the most commonly used techniques for the hardening of metal alloys.
The term hardened steel is often used for a medium or high carbon steel that has been given heat treatment and then quenching followed by tempering. The quenching results in the formation of metastable martensite, the fraction of which is reduced to the desired amount during tempering. This is the most common state for finished articles such as ...
Unlike differential hardening, where the entire piece is heated and then cooled at different rates, in flame hardening, only a portion of the metal is heated before quenching. This is usually easier than differential hardening, but often produces an extremely brittle zone between the heated metal and the unheated metal, as cooling at the edge ...
The quenching converts the billet's surface layer to martensite, and causes it to shrink. The shrinkage pressurizes the core, helping to form the correct crystal structures. The core remains hot, and austenitic. A microprocessor controls the water flow to the quench box, to manage the temperature difference through the cross-section of the bars.
The process was used throughout the ancient world, from Asia to Europe and Africa. Many different methods and cooling baths for quenching have been attempted during ancient times, from quenching in urine, blood, or metals like mercury or lead, but the process of tempering has remained relatively unchanged over the ages.
As with conventional quench and tempering the material being heat treated must be cooled from the austenitizing temperature quickly enough to avoid the formation of pearlite. The specific cooling rate that is necessary to avoid the formation of pearlite is a product of the chemistry of the austenite phase and thus the alloy being processed.