The strain hardening exponent (also called the strain hardening index), usually denoted , is a measured parameter that quantifies the ability of a material to become stronger due to strain hardening. Strain hardening (work hardening) is the process by which a material's load-bearing capacity increases during plastic (permanent) strain , or ...
The index n usually lies between the values of 2, for fully strain hardened materials, and 2.5, for fully annealed materials. It is roughly related to the strain hardening coefficient in the equation for the true stress-true strain curve by adding 2. [1] Note, however, that below approximately d = 0.5 mm (0.020 in) the value of n can surpass 3.
Here, n is the strain-hardening exponent and K is the strength coefficient. n is a measure of a material's work hardening behavior. Materials with a higher n have a greater resistance to necking. Typically, metals at room temperature have n ranging from 0.02 to 0.5. [3]
The name cam clay asserts that the plastic volume change typical of clay soil behaviour is due to mechanical stability of an aggregate of small, rough, frictional, interlocking hard particles. [3] The Original Cam-Clay model is based on the assumption that the soil is isotropic, elasto-plastic, deforms as a continuum, and it is not affected by ...
For annealed materials the Meyer hardness increases continuously with load due to strain hardening. [2] Based on Meyer's law hardness values from this test can be converted into Brinell hardness values, and vice versa. [3]
Work hardening, also known as strain hardening, is the process by which a material's load-bearing capacity (strength) increases during plastic (permanent) deformation. This characteristic is what sets ductile materials apart from brittle materials. [1] Work hardening may be desirable, undesirable, or inconsequential, depending on the application.
Thus the basic influence parameters for the forming limits are, the strain hardening exponent, n, the initial sheet thickness, t 0 and the strain rate hardening coefficient, m. The lankford coefficient, r, which defines the plastic anisotropy of the material, has two effects on the forming limit curve. On the left side there is no influence ...
Alternatively, if the yield stress, , is assumed to be at the 0.2% offset strain, the following relationship can be derived. [5] Note that is again as defined in the original Ramberg-Osgood equation and is the inverse of the Hollomon's strain hardening coefficient.