ISO 18265: "Metallic materials — Conversion of hardness values" (2013) ASTM E140-12B(2019)e1: "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" (2019)
This page was last edited on 16 November 2024, at 12:16 (UTC).; Text is available under the Creative Commons Attribution-ShareAlike 4.0 License; additional terms may apply.
Brinell hardness is sometimes quoted in megapascals; the Brinell hardness number is multiplied by the acceleration due to gravity, 9.80665 m/s 2, to convert it to megapascals. The Brinell hardness number can be correlated with the ultimate tensile strength (UTS), although the relationship is dependent on the material, and therefore determined ...
A Rockwell hardness tester. The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
Each of the ten hardness values in the Mohs scale is represented by a reference mineral, most of which are widespread in rocks. The Mohs scale is an ordinal scale . For example, corundum (9) is twice as hard as topaz (8), but diamond (10) is four times as hard as corundum.
When testing coatings, scratch hardness refers to the force necessary to cut through the film to the substrate. The most common test is Mohs scale, which is used in mineralogy. One tool to make this measurement is the sclerometer. Another tool used to make these tests is the pocket hardness tester. This tool consists of a scale arm with ...
The unit of hardness given by the test is known as the Vickers Pyramid Number (HV) or Diamond Pyramid Hardness (DPH). The hardness number can be converted into units of pascals, but should not be confused with pressure, which uses the same units. The hardness number is determined by the load over the surface area of the indentation and not the ...
Meyer's law is often used to relate hardness values based on the fact that if the weight is quartered, the diameter of the indenter is halved. For instance, the hardness values are the same for a test load of 3000 kgf with a 10 mm indenter and for a test load of 750 kgf with a 5 mm diameter indenter.