Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [1] [2]
Galvanic corrosion. Corrosion of an iron nail wrapped in bright copper wire, showing cathodic protection of copper; a ferroxyl indicator solution shows colored chemical indications of two types of ions diffusing through a moist agar medium. Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an electrochemical ...
Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture. Rust consists of hydrous iron (III) oxides (Fe 2 O 3 ·nH 2 O) and iron (III) oxide-hydroxide (FeO (OH), Fe (OH) 3), and is typically associated with the corrosion of refined iron.
Corrosion engineering is an engineering specialty that applies scientific, technical, engineering skills, and knowledge of natural laws and physical resources to design and implement materials, structures, devices, systems, and procedures to manage corrosion. [1] From a holistic perspective, corrosion is the phenomenon of metals returning to ...
Galvanic series. The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the ...
Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal. The driving power for pitting corrosion is the depassivation of a small area, which becomes anodic (oxidation reaction) while an unknown but potentially vast area becomes cathodic (reduction reaction), leading to ...
Tarnish is a surface phenomenon that is self-limiting, unlike rust. Only the top few layers of the metal react. The layer of tarnish seals and protects the underlying layers from reacting. Tarnish preserves the underlying metal in outdoor use, and in this form is called chemical patina [2]. Unlike wear patina necessary in applications such as ...
Stress corrosion cracking (SCC) is the growth of crack formation in a corrosive environment. It can lead to unexpected and sudden failure of normally ductile metal alloys subjected to a tensile stress, especially at elevated temperature. SCC is highly chemically specific in that certain alloys are likely to undergo SCC only when exposed to a ...