Settlement cracks usually show up as vertical lines or hairline cracks (small cracks that are under 1/10 of an inch or 2.5 millimeters wide), especially around weak spots like doors, windows, and ...
Scanning electron microscope image of fatigue striations produced from constant amplitude loading. The crack is growing from left to right. Striations are marks produced on the fracture surface that show the incremental growth of a fatigue crack. A striation marks the position of the crack tip at the time it was made.
Fatigue has traditionally been associated with the failure of metal components which led to the term metal fatigue. In the nineteenth century, the sudden failing of metal railway axles was thought to be caused by the metal crystallising because of the brittle appearance of the fracture surface, but this has since been disproved. [ 1 ]
Intergranular fatigue fracture involves cases in which the integranular fracture occurs as a result of cyclic loading, or fatigue. This specific type of intergranular fracture is often associated with improper materials processing or harsh environmental conditions where the grains are severely weakened. [ 6 ]
mild steel cracks in the presence of alkali (e.g. boiler cracking and caustic stress corrosion cracking) and nitrates; copper alloys crack in ammoniacal solutions (season cracking); high-tensile steels have been known to crack in an unexpectedly brittle manner in a whole variety of aqueous environments, especially when chlorides are present.
In true corrosion fatigue, the fatigue-crack-growth rate is enhanced by corrosion; this effect is seen in all three regions of the fatigue-crack growth-rate diagram. The diagram on the left is a schematic of crack-growth rate under true corrosion fatigue; the curve shifts to a lower stress-intensity-factor range in the corrosive environment.
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
It is the result of the process of fatigue due to rolling/sliding contact. [2] [3] The RCF process begins with cyclic loading of the material, which results in fatigue damage that can be observed in crack-like flaws, like white etching cracks. [2] These flaws can grow into larger cracks under further loading, potentially leading to fractures ...