6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
Elastic properties describe the reversible deformation (elastic response) of a material to an applied stress.They are a subset of the material properties that provide a quantitative description of the characteristics of a material, like its strength.
This page was last edited on 16 November 2024, at 12:16 (UTC).; Text is available under the Creative Commons Attribution-ShareAlike 4.0 License; additional terms may apply.
Aluminum: 95.7 - 98.7 Silicon: 0.60 - 1 Iron: ≤ 0.50 Magnesium: 0.40 - 0.80 Zinc: ≤ 0.25 Manganese: ... Elastic modulus: 69 GPa Shear modulus: 26 GPa Poisson's ratio:
The temper designation follows the cast or wrought designation number with a dash, a letter, and potentially a one to three digit number, e.g. 6061-T6. The definitions for the tempers are: [5] [6]-F : As fabricated-H : Strain hardened (cold worked) with or without thermal treatment -H1 : Strain hardened without thermal treatment
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Aluminum 1100–O (annealed) 0.20: 180 2024 aluminum alloy (heat treated—T3) 0.16: 690 5052-O 0.13 210 Aluminum 6061–O (annealed) 0.20: 205 Aluminum 6061–T6: 0.05: 410 Aluminum 7075–O (annealed) 0.17: 400 Brass, Naval (annealed) 0.49: 895 Brass 70–30 (annealed) 0.49: 900 Brass 85–15 (cold-rolled) 0.34: 580 Cobalt-base alloy (heat ...