White cast iron displays white fractured surfaces due to the presence of an iron carbide precipitate called cementite. With a lower silicon content (graphitizing agent) and faster cooling rate, the carbon in white cast iron precipitates out of the melt as the metastable phase cementite, Fe 3 C, rather than graphite. The cementite which ...
A casting defect is an undesired irregularity in a metal casting process. Some defects can be tolerated while others can be repaired, otherwise they must be eliminated. They are broken down into five main categories: gas porosity, shrinkage defects, mould material defects, pouring metal defects, and metallurgical defects.
Vitreous china is used in a variety of household and sanitaryware items such as basins, toilets, bidets, urinals and bathtubs. [6] [better source needed] Items that use vitreous china are usually ones that are best when kept clean and sanitary, with which a coating of vitreous china enamel helps.
The pits on the surface are often obscured by corrosion products. Pitting can be initiated by a small surface defect, being a scratch or a local change in the alloy composition (or local impurities, e.g. metallic sulfide inclusions such as MnS or NiS), [10] [11] or a damage to the protective coating. Polished surfaces display a higher ...
Anaerobic corrosion is evident as layers of metal sulfides and hydrogen sulfide smell. On cast iron, a graphitic corrosion selective leaching may be the result, with iron being consumed by the bacteria, leaving graphite matrix with low mechanical strength in place. Various corrosion inhibitors can be used to combat microbial corrosion.
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
White cast iron is composed mostly of a microstructure called ledeburite mixed with pearlite. Ledeburite is very hard, making cast iron very brittle. If the white cast iron has a hypoeutectic composition, it is usually tempered to produce malleable or ductile cast iron. Two methods of tempering are used, called "white tempering" and "black ...
Enamel over cast iron is a popular material for kitchen and bathroom sinks. Heavy and durable, these sinks can also be manufactured in a very wide range of shapes and colors. Like stainless steel, they are very resistant to hot or cold objects, but they can be damaged by sharp impacts and once the glass surface is breached, the underlying cast ...