AlSi10Mg is a lightweight, high-strength aluminium alloy that is widely used in the aerospace, automotive, and medical industries. Its unique combination of aluminium , silicon , and magnesium makes it an ideal material for additive manufacturing processes, such as 3D printing .
The solubility decreases very quickly with falling temperature and is only 0.08 percent by mass at 200 °C. Alloys without further alloying elements or impurities are then present in two phases with the-mixed crystal and thephase (Mg 2 Si). The latter has a melting point of 1085 °C and is therefore thermally stable.
Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si. At room temperature, silicon is practically insoluble. Aluminum cannot be dissolved in silicon at all, not even at high temperatures.
A Assuming an altitude of 194 metres above mean sea level (the worldwide median altitude of human habitation), an indoor temperature of 23 °C, a dewpoint of 9 °C (40.85% relative humidity), and 760 mmHg sea level–corrected barometric pressure (molar water vapor content = 1.16%).
Liquidus temperature curve in the binary glass system SiO 2-Li 2 O. For impure substances, e.g. alloys, honey, soft drink, ice cream, etc. the melting point broadens into a melting interval. If the temperature is within the melting interval, one may see "slurries" at equilibrium, i.e. the slurry will neither fully solidify nor melt.
The Gmelin rare earths handbook lists 1522 °C and 1550 °C as two melting points given in the literature, the most recent reference [Handbook on the chemistry and physics of rare earths, vol.12 (1989)] is given with 1529 °C.
The melting point (or, rarely, liquefaction point) of a substance is the temperature at which it changes state from solid to liquid. At the melting point the solid and liquid phase exist in equilibrium. The melting point of a substance depends on pressure and is usually specified at a standard pressure such as 1 atmosphere or 100 kPa.
The melting point (sometimes called liquefaction point) is the temperature and pressure at which a solid becomes a liquid. In commercial and industrial situations, the process of condensing a gas to liquid is sometimes referred to as liquefaction of gases.