The Flory–Fox equation relates the number-average molecular weight, M n, to the glass transition temperature, T g, as shown below: =, where T g,∞ is the maximum glass transition temperature that can be achieved at a theoretical infinite molecular weight and K is an empirical parameter that is related to the free volume present in the polymer sample.
Therefore, this polymer relies solely on physical anchor points. When heated up to Tg, the material abruptly changes from a rigid state to a tapered state (softens). To achieve the effect, the shape must be changed rapidly to avoid rearrangement of the segments of the polymer chains and immediately cool the material also very rapidly below Tg.
The glass transition of a liquid to a solid-like state may occur with either cooling or compression. [10] The transition comprises a smooth increase in the viscosity of a material by as much as 17 orders of magnitude within a temperature range of 500 K without any pronounced change in material structure. [11]
SAN is similar in use to polystyrene.Like polystyrene itself, it is transparent and brittle. The copolymer has a glass transition temperature greater than 100 °C owing to the acrylonitrile units in the chain, thus making the material resistant to boiling water.
Poly(p-phenylene oxide) (PPO), poly(p-phenylene ether) (PPE), poly(oxy-2,6-dimethyl-1,4-phenylene), often referred to simply as polyphenylene oxide, is a high-temperature thermoplastic with the general formula (C 8 H 8 O) n. It is rarely used in its pure form due to difficulties in processing.
Polyetherimide (PEI; branded as Ultem [1]) is an amorphous, amber-to-transparent thermoplastic with characteristics similar to the related plastic PEEK.When comparing PEI to PEEK, the former is cheaper but has lower impact strength and a tighter temperature range.
PTMC is a predominantly amorphous polymer in the relaxed state but it can present some crystallinity, particularly when the chains are stretched. [ 4 ] The polymer presents glass transition temperature ( T g {\displaystyle T_{g}} ) between -15 and -30 °C and melting temperature ( T m {\displaystyle T_{m}} ) ranging from 38 to 41°C.
This allows the approximation of Helmholtz free energy, which is the natural form of free energy from the Flory–Huggins lattice theory, to Gibbs free energy. ^ In fact, two of the sites adjacent to a polymer segment are occupied by other polymer segments since it is part of a chain ; and one more, making three, for branching sites, but only ...