The superficial Rockwell scales use lower loads and shallower impressions on brittle and very thin materials. The 45N scale employs a 45-kgf load on a diamond cone-shaped Brale indenter, and can be used on dense ceramics. The 15T scale employs a 15-kgf load on a 1 ⁄ 16-inch-diameter (1.588 mm) hardened steel ball, and can be used on sheet metal.
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
A test takes a mere 2 seconds and, using the standard probe D, leaves an indentation of just ~0.5 mm in diameter on steel or steel casting with a Leeb hardness of 600 HLD. By comparison, a Brinell indentation on the same material is ~3 mm (hardness value ~400 HBW 10/3000), with a standard-compliant measuring time of ~15 seconds plus the time ...
hardness, Rockwell, A scale: See Rockwell scale. HRB: hardness, Rockwell, B scale: See Rockwell scale. HRC: hardness, Rockwell, C scale: See Rockwell scale. HRS: hot rolled steel: HT TR: heat treat, heat treatment: H&T or H/T or HT: hardened and tempered: A form of heat treatment in which the metal is first hardened and then tempered. Compare N&T.
The Rockwell scale; The Durometer scale; The Barcol scale; ... Hardness scales may also refer to: Methods of measuring the deposit formation by hard water.
Rockwell built heavy-duty truck axles and drive-trains in the U.S., along with power windows, seats, and locks. The Rockwell Tripmaster trip recording system for commercial vehicles was released along with the Logtrak module for DOT log recording for fleets who successfully petitioned the DOT for paper logbook exemptions. Rockwell also built ...
Several such tests exist, wherein the examined material is indented until an impression is formed; these tests can be performed on a macroscopic or microscopic scale. When testing metals, indentation hardness correlates roughly linearly with tensile strength , [ 1 ] but it is an imperfect correlation often limited to small ranges of strength ...
The tests work on the basic premise of measuring the critical dimensions of an indentation left by a specifically dimensioned and loaded indenter. Common indentation hardness scales are Rockwell, Vickers, Shore, and Brinell, amongst others.