Osmium is a hard, brittle, blue-gray metal, and the densest stable element—about twice as dense as lead. The density of osmium is slightly greater than that of iridium ; the two are so similar (22.587 versus 22.562 g/cm 3 at 20 °C) that each was at one time considered to be the densest element.
The failure of a material is usually classified into brittle failure or ductile failure . Depending on the conditions (such as temperature, state of stress, loading rate) most materials can fail in a brittle or ductile manner or both. However, for most practical situations, a material may be classified as either brittle or ductile.
Embrittlement is used to describe any phenomena where the environment compromises a stressed material's mechanical performance, such as temperature or environmental composition. This is oftentimes undesirable as brittle fracture occurs quicker and can much more easily propagate than ductile fracture, leading to complete failure of the equipment.
Liquid metal embrittlement (also known as LME and liquid metal induced embrittlement) is a phenomenon of practical importance, where certain ductile metals experience drastic loss in tensile ductility or undergo brittle fracture when exposed to specific liquid metals.
Some metals that are generally described as ductile include gold and copper, while platinum is the most ductile of all metals in pure form. [4] However, not all metals experience ductile failure as some can be characterized with brittle failure like cast iron. Polymers generally can be viewed as ductile materials as they typically allow for ...
Some nonmetals (black P, S, and Se) are brittle solids at room temperature (although each of these also have malleable, pliable or ductile allotropes). From left to right in the periodic table, the nonmetals can be divided into the reactive nonmetals and the noble gases. The reactive nonmetals near the metalloids show some incipient metallic ...
Ductile iron is used in many piano harps (the iron plates which anchor piano strings). Ductile iron is used for vises. Previously, regular cast iron or steel was commonly used. The properties of ductile iron make it a significant upgrade in strength and durability from cast iron without having to use steel, which is expensive and has poor ...
The least brittle structural ceramics are silicon carbide (mainly by virtue of its high strength) and transformation-toughened zirconia. A different philosophy is used in composite materials, where brittle glass fibers, for example, are embedded in a ductile matrix such as polyester resin. When strained, cracks are formed at the glass–matrix ...