When a reinforced concrete member is put in tension, after cracking, the member elongates by widening of cracks and by formation of new cracks. Figure 1 Formation of internal cracks. Ignoring the small elastic strain in the concrete between the cracks, we can relate the crack width to the strain of the member by:
Cracks development occurs when early-age concrete is insufficiently protected against desiccation and too much water evaporates with heat because of unfavorable meteorological conditions: e.g, high temperature, direct solar insolation, dry air, low relative humidity, and high wind speed during summer, or in hot conditions. Curing is intended to ...
Typical crack pattern of the alkali-silica reaction (ASR). The gel exudations through the concrete cracks have a characteristic yellow color and a high pH. The fatty aspect of the exudations imbibing the concrete porosity along the cracks is also a distinctive feature of ASR. The alkali-silica reaction as a chemical cycle process
Concrete fracture analysis is part of fracture mechanics that studies crack propagation and related failure modes in concrete. [17] As it is widely used in construction, fracture analysis and modes of reinforcement are an important part of the study of concrete, and different concretes are characterized in part by their fracture properties. [ 18 ]
Concrete has a very low coefficient of thermal expansion, and as it matures concrete shrinks. All concrete structures will crack to some extent, due to shrinkage and tension. Concrete which is subjected to long-duration forces is prone to creep. The density of concrete varies, but is around 2,400 kilograms per cubic metre (150 lb/cu ft). [1]