Barcol hardness is measured on a scale from 0 to 100 with the typical range being between 50B and 90B. A measurement of 60B is roughly equivalent to a Shore hardness of 80D or a Rockwell hardness M100. [4] [6] As defined in ASTM D 2583 the scale divisions from 0-100 should each indicate a depth of 0.0076 mm or the equivalent 0.0003 inches. [7]
The VPAM scale as of 2009 runs from 1 to 14, with 1-5 being soft armor, and 6-14 being hard armor. [1] Tested armor must withstand three hits, spaced 120 mm (4.7 inches) apart, of the designated test threat with no more than 25 mm (0.98 inches) of back-face deformation in order to pass.
A first-order estimate of the relation between ASTM D2240 type D hardness (for a conical indenter with a 15° half-cone angle) and the elastic modulus of the material being tested is [10] = (+ +), where is the ASTM D2240 type D hardness, and is in MPa.
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
Common greases are in the range 1 through 3. Those with a NLGI No. of 000 to 1 are used in low viscosity applications. Examples include enclosed gear drives operating at low speeds and open gearing. Grades 0, 1 and 2 are used in highly loaded gearing. Grades 1 through 4 are often used in rolling contact bearings. Greases with a higher number ...
The interaction of the drum, steel balls and the samples at the bottom of the drum causes further abrading and grinding. [5] The complete test requires 500 drum revolutions at a speed of 30-33 revolutions per minute. [6] Crushed sample is then separated from fine dust on a sieve, washed, dried and weighed. [6]
The Janka hardness test results tabulated below followed ASTM D 1037-12 testing methods. Lumber stocks tested range from 1" to 2" (25–50 mm) thick. The tabulated Janka hardness numbers are an average. There is a standard deviation associated with each species, but these values are not given. [citation needed] No testing was done on actual ...
According to ASTM A370, [12] the standard specimen size for Charpy impact testing is 10 mm × 10 mm × 55 mm. Subsize specimen sizes are: 10 mm × 7.5 mm × 55 mm, 10 mm × 6.7 mm × 55 mm, 10 mm × 5 mm × 55 mm, 10 mm × 3.3 mm × 55 mm, 10 mm × 2.5 mm × 55 mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for ...