T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10]
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [8] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.
T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
5052 is an aluminium–magnesium alloy, ... Ultimate MPa (PSI) Yield MPa (PSI) Tensile Strength acc. ASTM B209 [KSI] Yield Strength acc. ASTM B209 [KSI] O: 195 (28000)
2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
Alloy 5083 retains exceptional strength after welding. It has the highest strength of the non-heat treatable alloys with an Ultimate Tensile Strength of 317 MPa or 46000 psi and a Tensile Yield Strength of 228 MPa or 33000 psi. It is not recommended for use in temperatures in excess of 65 °C. [2]
7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]
The yield strength or yield stress is a material property and is the stress corresponding to the yield point at which the material begins to deform plastically. The yield strength is often used to determine the maximum allowable load in a mechanical component, since it represents the upper limit to forces that can be applied without producing ...