2024 aluminium alloy is an aluminium alloy, ... Aluminium alloy 2024 has a density of 2.78 g/cm 3 ... and yield strength of at least 270–280 MPa (39–40 ksi). ...
T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10]
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Typical material properties for 6005 aluminium alloy include: [2] Density: 2.70 g/cm 3, or 169 lb/ft 3. Young's modulus: 69 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Expansion: 23 μm/m-K.
Typical material properties for 6060 aluminum alloy include: [2] Density: 2.710 g/cm 3, or 169 lb/ft 3. Young's modulus: 70 GPa, or 10 Msi, or 303 EMEC; Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2] Strength allowables for this alloy are provided in Metallic Materials Properties Development and Standardization for design. [3]
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
The yield strength of pure aluminium is 7–11 MPa, while aluminium alloys have yield strengths ranging from 200 MPa to 600 MPa. [32] Aluminium is ductile , with a percent elongation of 50-70%, [ 33 ] and malleable allowing it to be easily drawn and extruded . [ 34 ]