Vicat softening temperature or Vicat hardness is the determination of the softening point for materials that have no definite melting point, such as plastics. It is taken as the temperature at which the specimen is penetrated to a depth of 1 mm by a flat-ended needle with a 1 mm 2 circular or square cross-section.
Melting temperature (T m) 150 °C [citation needed] Glass transition temperature (T g) 106–115 °C: Vicat softening point—50 N (Vicat B)
Polycarbonate is relatively difficult for casual hobbyists to print compared to thermoplastics such as Polylactic acid (PLA) or Acrylonitrile butadiene styrene (ABS) because of the high melting point, difficulty with print bed adhesion, tendency to warp during printing, and tendency to absorb moisture in humid environments. Despite these issues ...
The softening point is the temperature at which a material softens beyond some arbitrary softness. [1] It can be determined, for example, by the Vicat method (ASTM-D1525 or ISO 306), Heat Deflection Test (ASTM-D648) or a ring and ball method (ISO 4625 or ASTM E28-67/E28-99 or ASTM D36 or ASTM D6493 - 11 or JIS K 6863).
Melting point: 100 °C (212 °F) to 260 °C (500 °F) [5] Effective heat of combustion 17.95 MJ/kg Specific heat (c) 0.9 kJ/(kg·K) ... Vicat B [32] °C 65–100
General-purpose polystyrene is clear, hard, and brittle. It is an inexpensive resin per unit weight. It is a poor barrier to air and water vapor and has a relatively low melting point. [6] Polystyrene is one of the most widely used plastics, with the scale of its production being several million tonnes per year. [7]
This interferes with crystallization and lowers the polymer's melting temperature. In general, such PET is known as PETG or PET-G (polyethylene terephthalate glycol-modified). It is a clear amorphous thermoplastic that can be injection-molded, sheet-extruded or extruded as filament for 3D printing .
Borosilicate is referred to as "hard glass" and has a higher melting point (approximately 3,000 °F / 1648 °C) than "soft glass", which is preferred for glassblowing by beadmakers. Raw glass used in lampworking comes in glass rods for solid work and glass tubes for hollow work tubes and vessels/containers. Lampworking is used to make complex ...