Polyvinyl alcohol (PVOH, PVA, or PVAl) is a water-soluble synthetic polymer. It has the idealized formula [CH 2 CH(OH)] n . It is used in papermaking , textile warp sizing , as a thickener and emulsion stabilizer in polyvinyl acetate (PVAc) adhesive formulations, in a variety of coatings, and 3D printing .
Vinyl polymers are subject of several structural variations, which greatly expands the range of polymers and their applications. With the exception of polyethylene, vinyl polymers can arise from head-to-tail linking of monomers, head-to-head combined with tail-to-tail, or a mixture of those two patterns. Additionally the substituted carbon center in such polymers is stereogenic (a "chiral center")
Vinyl alcohol, also called ethenol (IUPAC name; not ethanol) or ethylenol, is the simplest enol. With the formula C H 2 CH O H , it is a labile compound that converts to acetaldehyde immediately upon isolation near room temperature. [ 1 ]
Formvar refers to any of several thermoplastic resins that are polyvinyl formals, which are polymers formed from polyvinyl alcohol and formaldehyde as copolymers with polyvinyl acetate. They are typically used as coatings, adhesives , and molding materials.
The following other wikis use this file: Usage on ar.wikipedia.org بولي فاينيل الكحول; Usage on az.wikipedia.org Polivinil spirti
For instance, polyvinyl alcohol is (CH 2 CHOH) n with n hydroxyl groups where n can be in the thousands. Cellulose is a polymer with many hydroxyl groups, but it is not referred to as a polyol. Polyols from recycled or renewable sources
Vinylon, also known as Vinalon (more common in Korean sources), is a synthetic fiber produced from reaction between polyvinyl alcohol (PVA) fiber and formaldehyde. Chemically it is polyvinyl formal (PVF). Vinylon was first developed in Japan in 1939 by Ichiro Sakurada, Ri Sung-gi, and H. Kawakami. [1]
The degree of polymerization of polyvinyl acetate is typically 100 to 5000, while its ester groups are sensitive to base hydrolysis and slowly convert PVAc into polyvinyl alcohol and acetic acid. The glass transition temperature of polyvinyl acetate is between 30 and 45 °C depending on the molecular weight.