Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
Corrosion engineering is an engineering specialty that applies scientific, technical, engineering skills, and knowledge of natural laws and physical resources to design and implement materials, structures, devices, systems, and procedures to manage corrosion. [1]
What type of metal(s) to use is readily determined by following the galvanic series. For example, zinc is often used as a sacrificial anode for steel structures. Galvanic corrosion is of major interest to the marine industry and also anywhere water (containing salts) contacts pipes or metal structures.
Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture.Rust consists of hydrous iron(III) oxides (Fe 2 O 3 ·nH 2 O) and iron(III) oxide-hydroxide (FeO(OH), Fe(OH) 3), and is typically associated with the corrosion of refined iron.
Cathodic Protection: Cathodic protection is a technique used to protect metals from corrosion by applying a small electrical current to the metal surface. This technique can also help prevent SCC by reducing the corrosion potential of the metal. [7] Environmental Controls: Controlling the environment around the metal can help prevent SCC.
The process of pit nucleation is initiated by the depassivation of the protective oxide layer isolating the metal substrate from the aggressive solution. The depassivation of the protective oxide layer is the less properly understood step in pitting corrosion and its very local and random appearance probably its most enigmatic characteristic.
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Metallurgical failure analysis is the process to determine the mechanism that has caused a metal component to fail.It can identify the cause of failure, providing insight into the root cause and potential solutions to prevent similar failures in the future, as well as culpability, which is important in legal cases. [1]