A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
Mohs hardness [1] Vickers hardness (MPa) [1] Brinell hardness (MPa) [1] Brinell hardness (MPa) [note 1] [2] 3: Li: lithium: 0.6: 5: 4: Be: beryllium: 5.5: 1670: 590 ...
A Rockwell hardness tester. The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
ASTM A956 “Standard Test Method for Leeb Hardness Testing of Steel Products” ASTM E140 - 12be1 "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" Official international standards projects:
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
The hardness of abrasion resistant steel is determined by a Brinell hardness test. This test uses a small steel ball to inflict force on a material. The indentation created by the steel ball is then measured and used to calculate Brinell hardness number (BHN). [3]